AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod

Gute Qualität Kaltbezogenes Stahlrohr en ventes
Gute Qualität Kaltbezogenes Stahlrohr en ventes
Ich bin online Chat Jetzt

AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod

China AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod fournisseur
AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod fournisseur AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod fournisseur

Großes Bild :  AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod

Produktdetails:

Herkunftsort: Mainland China
Markenname: UST
Zertifizierung: ISO 9001:2008
Modellnummer: ASTM O1

Zahlung und Versand AGB:

Min Bestellmenge: 3 metrische Tonnen
Preis: USD 1200-3000 / Metric Ton
Verpackung Informationen: In der Standardexportverpackung und im seetauglichen Material mit dem rechteckigen Formbündel, bedec
Lieferzeit: 15-35 giorni
Zahlungsbedingungen: L/C, T/T, D/A, D/P
Versorgungsmaterial-Fähigkeit: 1000 metrische Tonnen pro Monat
Contact Now
Ausführliche Produkt-Beschreibung
Matrial: Werkzeugstahl Standard: GB, ASTM, LÄRM, JIS
Grad: O1 / 1,2510 Durchmesser: 20-1000mm
Länge: Unterhalb 16 Meter Shape: Rundeisen
Techniken: Kaltbezogen; Warm gewalzt; Kaltgewalzt; Geschmiedet Oberfläche: Schwarz, hell, Polier, abgezogen oder auf Anfrage
Ultraschallprüfung: 100% UT geführt Verarbeitung: Getempert oder gelöscht und gemildert zur Verfügung gestellt
Ende: Abgeschrägtes, einfaches Ende wie erforderlich Qualitäts-Inspektion: SGS, BV etc.
Bedienung: Ausschnittservice und Inspektion der 3. Partei wird zur Verfügung gestellt

INTRODUCTION

 

-AISI O1 tool steel has deep hardening properties with fine grain structure with unusual toughness.

-AISI O1 tool steel offers good durability, gives excellent wear resistance and holds a good cutting edge.

-AISI O1 cold work tool steels also has good response to heat treatment with small dimensional changes.

 

We are a better choice of O1 oil tool steel materials supplier with reliable quality and sales service. AISI Tool steel O1 is available in standard de-carb free rounds, flats and squares, as well as the largest size selection in O1 oil steel ground flat stock and drill rod of all the tool steel grades, or as per customized requirements.

 

 

APPLICATIONS

 

O1 steels are mainly used for short run tooling for cold forming dies, blanking dies, and cutting tools operating at ambient temperature.

 

Typical applications for O1 tool steel are blanking, forming, and trim dies, gages, slitting cutters, punches, bolster dies, knock-out pins, thread roll dies, bending dies, plastic mold dies, shims, cams, machine ways, stamps, machine parts, jigs, cutter templates, swaging dies, etc.

 

Steel Grade 1.2510 Application Tool steel, Mold Steel
Shape Round Bar Standard GB, ASTM, DIN,JIS
Dimension Φ20-1000 mm; length below 16m Surface Black, Bright, Polished, Peeled
Technique Cold drawn; Hot rolled; Forged Ultrasonic Test 100% UT Passed

 

DELIVERY CONDITIONS

 

  Diameter (mm)
Cold drawn 10-100
Peeled 30-160
Grinded 10-600
Turned 130-1600
Hot Rolled 20-280
Hot Forged 130-1000

 

-EAF+(ESR) or EAF+LF+VD+(ESR)

-HOT rolled; Cold rolled; Forged; Cold Drawn

-Heat Treatment: Untreated, Annealing, N+T, Q+T

-Smelting: EAF+LF+VD (+ESR)

-Surface Finish: Black, Rough Machined, Peeled, Turned or as per given requirements

-UT 100% passed

-Cutting service provided

-Third Party inspection is acceptable (SGS, BV etc.)

 

EQUIVALENT GRADES

 

AISI/SAE DIN JIS GB
O1 1.2510 SKS3 9CrWMn

 

CHEMICAL COMPOSITION (%)

 

C Si Mn P S Cr V W

0.85

1.00

0.10

0.50

1.00

1.40

0.030

0.030

0.40

0.70

0.30

0.40

0.60

 

MECHANICAL PROPERTIES

Properties Metric Imperial
Hardness, Brinell (soft annealed -delivery condition) 190 190
Hardness, Rockwell C (tempering temp 300-1200°F) 34.0-64.0 34.0-64.0
Elastic modulus (hardened to 62 HRC) 193 GPa 28000 ksi
Elastic modulus (@399°C/750°F, hardened to 62 HRC ) 172 GPa 25000 ksi
Elastic modulus (@191°C/375°F, hardened to 62 HRC) 186 GPa 27000 ksi
Compressive yield strength (0.2%, hardened to 50 HRC) 1350 MPa 196000 psi
Compressive yield strength (0.2%, hardened to 55 HRC) 1800 MPa 261000 psi
Compressive yield strength (0.2%, hardened to 60 HRC) 2150 MPa 312000 psi
Compressive yield strength (0.2%, hardened to 62 HRC) 2200 MPa 319000 psi

 

 

 

PROCESSING

 

Forging of AISI O1 Tool Steel

Heating for forging of oil tool steel O1 must be done slowly and uniformly. Forging of alloy O1 steels can be performed at 980-1000°C, and reheat as often as necessary. But not forge below 800°C. After forging AISI O1 tool steel, cool slowly in lime, mica, dry ashes or furnace. ASTM O-1 tool steels should always be annealed after forging.

 

AISI O1 Tool Steel Heat Treatment

 

Anneal
Annealing must be performed after hot working and before re-hardening.

Heat at a rate not exceeding 222°C per hour to 802-816°C, and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 28°C per hourto 538°C. Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 212 HBW.

 

Stress Relief of Unhardened Material
Heat slowly to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.

 

Hardening
-Preheat: Warm slightly before charging into the preheat furnace, which should be operating at about 1100°-1200°F.
-Hardening: Heat to 1475 to 1500° F. Soak at heat for 30 minutes per inch of thickness.
-Quench: Quench O1 steel in warm oil and allow to cool in the oil until a temperature of 125°-150°F has been reached, or to where the part can be held in the bare hand, and temper immediately.
-Temper: Normally oil hardening steels need to be single tempered only. However, double tempering may sometimes be preferred. Soak at heat for 2 hours per inch of thickness for each temper. Air cool to room temperature between tempers. The normal tempering range for this grade is 300 to 450° F.

 

Stress Relief Temper
A stress relief temper for hardened material is strongly recommended after significant grinding, or welding, or EDM. Select a temperature that is 25 or 50° F lower than the last tempering temperature used.

 

AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod

 

What we can offer?

-We offer a wide range of steel products in a wide variety of dimensions and executions, according to the common international specifications or customize.

-Machining and heat treatment are available.

-Also, we advise you in choosing the right materials.

 

Shape Available

  • Solid round bar
  • Flat bar
  • Square bar
  • Hexagon bar
  • Block
  • Plate
  • Sheet
  • Wire rod
  • Strip

 

Our Advantages

  • High mechanical property and quenching, enable the surface share equal hardness after deal with it
  • Good polishing and low roughness
  • Making the heat-treatment to harden condition before using it
  • Competitive price
  • Fast production lead-time
  • All the material are inspected with 3 times to meet the highly standards
  • Pure steel quality & stable quality to be guarantee
 

OUR MAIN PRODUCTS ARE LISTED AS BELOW

 

AISI O1 / DIN EN 95MnWCr5 1.2510 Cold-Work Tool Steel Bar / Rod

 

Notes:

Available Size:
-Round: Dia. 20-1000 mm
-Flat: T. 10-120 mm x W. 60-810 mm
-Block: T. 80-1200 mm x W. 100-1600 mm

 

PAYMENT AND SHIPPING

 

1. Both T/T and L/C will be acceptable

2. Trade Terms: FOB, CIF, CFR

3. The delivery will be in 10-15 days if have stock; For customized items, the delivery will be negotiated by both parties

4. Shipping by sea freight from Shanghai Port (PRC) for Bulk orders, by airfreight or express for samples

 

COMPANY INFORMATION

 

Shanghai Unite Steel Trading Co., Ltd

We are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china.

What’s more, we have built long, deep and close business relationship with dozens of steel company, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!

 

FAQ

 

Q: Are you a manufacturer or merely a trader?
A: We are group of companies and owned manufacturer bases and trading company. We specialized in special steel which include alloy structural steel and carbon steel and stainless steel, etc. All material are with high quality and competitive price.

Q: How do you guarantee the quality of your product?
A: Firstly, we can provide the certificates from the third party, such as TUV, CE, if you need. Secondly, we have a complete set of inspection system and every process is checked by QC. Quality is the lifeline of enterprise survival.

Q: Delivery time?
A: We have ready stock for most of material grades in our warehouse. If the material doesn't have stock, the delivery lead time is about 5-30 days after receiving your prepayment or firm order.

Q: What is the payment term?
A: T/T or L/C.

Q: Can we visit your company and factory?
A: Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.

 

CONTACT US

 

We are happy to answer your questions and make you an offer for these and other materials. Contact us now for more information.

 

Your Contact Person

Ms Chilli Ho

Phone/Wechat/Whatsapp +86-181-0187-5575

Skype: chilli.ho@outlook.com

Email: chilli.ho@shunitesteel.com

Kontaktdaten
SHANGHAI UNITE STEEL TRADING CO., LTD

Ansprechpartner: Chilli.ho

Telefon: +8618101875575

Senden Sie Ihre Anfrage direkt an uns (0 / 3000)